The use of gadolinium-carbon nanostructures to magnetically enhance stem cell retention for cellular cardiomyoplasty

In this work, the effectiveness of using Gadonanotubes (GNTs) with an external magnetic field to improve retention of transplanted adult mesenchymal stem cells (MSCs) during cellular cardiomyoplasty was evaluated. As a high-performance T1-weighted magnetic resonance imaging (MRI) cell tracking label, the GNTs are gadolinium-loaded carbon nanotube capsules that render MSCs magnetic when internalized. MSCs were internally labeled with either superparamagnetic GNTs or colloidal diamagnetic lutetium (Lu). In vitro cell rolling assays and ex vivo cardiac perfusion experiments qualitatively demonstrated increased magnetic-assisted retention of GNT-labeled MSCs. Subsequent in vivo epicardial cell injections were performed around a 1.3 T NdFeB ring magnet sutured onto the left ventricle of female juvenile pigs (n = 21). Cell dosage, magnet exposure time, and endpoints were varied to evaluate the safety and efficacy of the proposed therapy. Quantification of retained cells in collected tissues by elemental analysis (Gd or Lu) showed that the external magnet helped retain nearly three times more GNT-labeled MSCs than Lu-labeled cells. The sutured magnet was tolerated for up to 168 h; however, an inflammatory response to the magnet was noted after 48 h. These proof-of-concept studies support the feasibility and value of using GNTs as a magnetic nanoparticle facilitator to improve cell retention during cellular cardiomyoplasty

A New High-Performance Gadonanotube-Polymer Hybrid Material for Stem Cell Labeling and Tracking by MRI

A gentle, rapid method has been developed to introduce a polyacrylic acid (PAA) polymer coating on the surface of gadonanotubes (GNTs) which significantly increases their dispersibility in water without the need of a surfactant. As a result, the polymer, with its many carboxylic acid groups, coats the surface of the GNTs to form a new GNT-polymer hybrid material (PAA-GNT) which can be highly dispersed in water (ca. 20 mg·mL−1) at physiological pH. When dispersed in water, the new PAA-GNT material is a powerful MRI contrast agent with an extremely short water proton spin-lattice relaxation time (T1) which results in a T1-weighted relaxivity of 150 mM−1·s−1 per Gd3+ ion at 1.5 T. Furthermore, the PAA-GNTs have been used to safely label porcine bone-marrow-derived mesenchymal stem cells for magnetic resonance imaging. The labeled cells display excellent image contrast in phantom imaging experiments, and transmission electron microscopy images of the labeled cells reveal the presence of highly dispersed PAA-GNTs within the cytoplasm with 1014 Gd3+ ions per cell

Surfactant-free Gd3+-ion-containing carbon nanotube MRI contrast agents for stem cell labeling

There is an ever increasing interest in developing new stem cell therapies. However, imaging and tracking stem cells in vivo after transplantation remains a serious challenge. In this work, we report new, functionalized and high-performance Gd3+-ion-containing ultra-short carbon nanotube (US-tube) MRI contrast agent (CA) materials which are highly-water-dispersible (ca. 35 mg ml−1) without the need of a surfactant. The new materials have extremely high T1-weighted relaxivities of 90 (mM s)−1 per Gd3+ ion at 1.5 T at room temperature and have been used to safely label porcine bone-marrow-derived mesenchymal stem cells for MR imaging. The labeled cells display excellent image contrast in phantom imaging experiments, and TEM images of the labeled cells, in general, reveal small clusters of the CA material located within the cytoplasm with 109 Gd3+ ions per cell