Does the acidity of self-etching primers affect bond strength and surface morphology of enamel?

Purpose: This study examined the ultrastructure and microtensile bond strengths (TBS) of self-etching (with different acidity) and conventional adhesive systems bonded to unground enamel. Materials and Methods: Resin composite (Filtek Z250) buildups were bonded to unground enamel surfaces of third molars after adhesive application with the following materials: Clearfil SE Bond (CSE); Optibond Solo Plus Self-Etch (OP); Tyrian Self Priming Etching (TY), and the controls Scotchbond Multi-Purpose Plus (SBMP) and Single Bond (SB). Six teeth were assigned to each material. After storage in water for 24 h at 37 degrees C, the bonded specimens were sectioned into beams of approximately 0.8 mm(2) and subsequently subjected to mu TBS testing at a crosshead speed of 0.5 mm/min. The average values were subjected to one-way ANOVA (alpha = 0.05). The effect of surface conditioning of each material was observed under scanning electron microscopy (SEM). Results: The highest resin-enamel bond strength was observed for SBMP (22.7 +/- 5.2) and SB (26.7 +/- 5.2 MPa). The lowest mean bond strengths were 10.9 +/- 3.2 and 7.8 +/- 1.5 MPa for TY and OP, respectively. CSE showed an intermediate performance (18.7 +/- 4.6 MPa). An overall increase in porosity was evident along the entire enamel surface treated with the self-etching primers; however, no selective demineralization similar to that with 35% phosphoric acid was observed. Conclusion: The highest bond strength means and the more retentive etching pattern were observed for the two-step etch-and-rinse adhesives. Among the self-etching systems studied, Clearfil SE Bond should be preferred.82758

A 12-month clinical evaluation of pit-and-fissure sealants placed with and without etch-and-rinse and self-etch adhesive systems in newly-erupted teeth

OBJECTIVES: The objective of this one-year clinical study was to investigate the effect of two adhesive systems (Adper Single Bond, a two-step etch-and-rinse and Clearfil SE Bond, a two-step self-etch system) on pit-and-fissure sealant retention in newly-erupted teeth. This study compared the success of the sealants in mesial and distopalatal grooves with and without these two adhesive systems. MATERIAL AND METHODS: In a clinical trial, 35 children aged 6-8 years undergoing sealant placement were recruited. This one-year clinical study scored 70 mesial and 70 distopalatal sealants of newly-erupted permanent maxillary first molar, with a split-mouth design. All children received sealant alone in one permanent maxillary molar tooth. Children were randomized into two groups. One group received Self-Etch (SE) bond plus sealant and the other group received Single Bond plus sealant in another permanent maxillary molar tooth. Clinical evaluation at 3, 6 and 12 months was performed and the retention was studied in terms of the success and failure. RESULTS: The success rate of sealant in the distopalatal groove, using SEB at 3, 6 and 12 months was 93.3% (95% CI: 68.0, 99.8), 73.3% (95% CI: 44.9, 92.2) and 66.7% (95% CI: 38.4, 88.2), respectively. It was greater than that of the distopalatal groove in SB group with a success rate of 62.5% (95% CI: 35.4, 84.8), 31.3% (95% CI: 11.8, 58.7) and 31.3% (95% CI: 11.8, 58.7), at the three evaluation periods. The success rate of sealant in the mesial groove using SEB was 86.6% (95% CI: 59.5, 98.3), 53.3% (95% CI: 26.6, 78.7) and 53.3% (95% CI: 26.6, 78.7), while this was 100% (95% CI: 79.4, 100.0), 81.3% (95% CI: 54.4, 96.0) and 81.3% (95% CI: 54.4, 96.0) using SB, at 3, 6 and 12-month evaluation periods. CONCLUSIONS: These results support the use of these two bonding agents in pit-and-fissure sealants under both isolated and contaminated conditions. Further, SE bond seemed to be less sensitive to moisture contamination

Effect of the application time of phosphoric acid and self-etch adhesive systems to sclerotic dentin

OBJECTIVES: To evaluate the effect of application time on the resin-dentin bond strength (µTBS) and etching pattern of adhesive systems applied on sclerotic dentine. MATERIAL AND METHODS: A total of forty-two bovine incisors had their roots removed. The 1-step self-etch GO (SDI), the 2-step self-etch Adper SE Bond (3MESPE) and the 35% phosphoric acid (3MESPE) from the 2-step etch-and-rinse Adper Single Bond 2 (3MESPE) were applied on the bovine incisal surfaces according to the manufacturer's instructions or duplicating the recommended conditioning time. After adhesive application, thirty teeth were restored with composite resin, stored for 24 h in distilled water at 37º C, and sectioned into resin-dentin bonded sticks (0.8 mm(2)) and tested according to the µTBS at 0.5 mm/min. The etching pattern of the remaining twelve teeth (n=4 for each material) was examined under scanning electron microscopy. Each tooth was divided into a buccal-to-lingual direction into three thirds, and each third randomly assigned to the groups: control (no treatment), according to the manufacturers' instructions and duplicating the recommended application time. The µTBS and the relative percentage of the tubule area opening were evaluated by two-way repeated measures ANOVA and Tukey's tests (α=0.05). RESULTS: The duplication of the conditioning time favored only the GO adhesive (p<0.05). Both application methods significantly increased the tubule area opening (p<0.05) compared to the controls. CONCLUSIONS: The efficacy of duplicating the conditioning time was only effective for the 1-step self-etch adhesive system tested

Review of Matrix Metalloproteinases’ Effect on the Hybrid Dentin Bond Layer Stability and Chlorhexidine Clinical Use to Prevent Bond Failure

This review describes the relationship between dentin collagen hybrid bond layer degradation and the Matrix Metalloproteinases (MMPs) after their release by acid etch and rinse adhesives and self etching bonding adhesives that can reduce the bond stability over time. MMP-2, MMP-8 and MMP-9 are indicated as the active proteases that breakdown the collagen fibrils in the hybrid bond layer. Phosphoric acid in the acid etch and rinse bonding process and acid primers in the self etch process are implicated in the release of these proteases and their activation by several non-collagen proteins also released from dentin by the etching. MMPs are released in saliva by salivary glands, by cells in the gingival crevices to crevicular fluid and by pulpal odontoblasts cells to the dentinal fluids. These sources may affect the hybrid layer also. Evidence of the bond strength deterioration over time and the ability of Chlorhexidine to prevent bond deterioration by inhibiting MMP action are discussed. Dentin Bonding procedure utilizing Chlorhexidine for different application times and concentrations are being developed. The application of 2% Chlorhexidine to the phosphoric acid etch surface after rinsing off the acid is the only procedure that has been clinically tested for a longer period of time and shown to prevent bond strength degradation so far. The adoption of this procedure is recommended as means of improving bond stability at this time