Effect of gallium doping on the characteristic properties of polycrystalline cadmium telluride thin film
Ga-doped CdTe polycrystalline thin films were successfully electrodeposited on glass/fluorine doped tin oxide (FTO) substrates from aqueous electrolytes containing cadmium nitrate (Cd(NO3)2⸱4H2O) and tellurium oxide (TeO2). The effects of different Ga-doping concentrations on the CdTe:Ga coupled with different post-growth treatments were studied by analysing the structural, optical, morphological and electronic properties of the deposited layers using X-ray diffraction (XRD), ultraviolet-visible spectrophotometry, scanning electron microscopy, photoelectrochemical cell measurement and direct-current conductivity test respectively. XRD results show diminishing (111)C CdTe peak above 20 ppm Ga-doping and appearance of (301)M GaTe diffraction above 50 ppm Ga-doping indicating the formation of two phases; CdTe and GaTe . Although, reductions in the absorption edge slopes were observed above 20 ppm Ga-doping for the as-deposited CdTe:Ga layer, no obvious influence on the energy gap of CdTe films with Ga-doping were detected. Morphologically, reductions in grain size were observed at 50 ppm Ga-doping and above with high pinhole density within the layer. For the as-deposited CdTe:Ga layers, conduction type change from n- to p- were observed at 50 ppm, while the n-type conductivity were retained after post-growth treatment. Highest conductivity was observed at 20 ppm Ga-doping of CdTe. These results are systematically reported in this pape
Improvement of composition of CdTe thin films during heat treatment in the presence of CdCl2
CdCl2 treatment is a crucial step in development of CdS/CdTe solar cells. Although this rocessing step has been used over a period of three decades, full understanding is not yet achieved. This paper reports the experimental evidence for improvement of composition of CdTe layers during CdCl2 treatment. This investigation makes use of four selected analytical techniques; Photo-electro-chemical (PEC) cell, X-ray diffraction (XRD), Raman spectroscopy and Scanning electron microscopy (SEM). CdTe layers used were electroplated using three Cd precursors; CdSO4, Cd(NO3)2 and CdCl2. Results show the improvement of stoichiometry of CdTe layers during CdCl2 treatment through chemical reaction between Cd from CdCl2 and elemental Te that usually precipitate during CdTe growth, due to its natural
behaviour. XRD and SEM results show that the low-temperature (~85ÂşC) electroplated CdTe layers consist of ~(20-60) nm size crystallites, but after CdCl2 treatment, the layers show drastic recrystallisation with grains becoming a few microns in size. These CdCl2 treated
layers are then comparable to high temperature grown CdTe layers by the size of grains