High pressure phases in highly piezoelectric Pb(Zr0.52Ti0.48)O3

Two novel room-temperature phase transitions are observed, via synchrotron x-ray diffraction and Raman spectroscopy, in the Pb(Zr0.52Ti0.48)O3 alloy under hydrostatic pressures up to 16 GPa. A monoclinic (M)-to-rhombohedral (R1) phase transition takes place around 2-3 GPa, while this R1 phase transforms into another rhombohedral phase, R2, at about 6-7 GPa. First-principles calculations assign the R3m and R3c symmetry to R1 and R2, respectively, and reveal that R2 acts as a pressure-induced structural bridge between the polar R3m and a predicted antiferrodistortive R-3c phase.Comment: REVTeX, 4 pages with 3 figures embedded. Figs 1 and 3 in colo

Evidence for MBM_B and MCM_C phases in the morphotropic phase boundary region of (1−x)[Pb(Mg1/3Nb2/3)O3]−xPbTiO3(1-x)[Pb(Mg_{1/3}Nb_{2/3})O_3]-xPbTiO_3 : A Rietveld study

We present here the results of the room temperature dielectric constant measurements and Rietveld analysis of the powder x-ray diffraction data on $(1-x)[Pb(Mg_{1/3}Nb_{2/3})O_3]-xPbTiO_3$(PMN-$x$PT) in the composition range $0.20 \leq x \leq 0.45$ to show that the morphotropic phase boundary (MPB) region contains two monoclinic phases with space groups Cm (or $M_B$ type) and Pm (or $M_C$ type) stable in the composition ranges $0.27 \leq x \leq 0.30$ and $0.31 \leq x \leq 0.34$, respectively. The structure of PMN-$x$PT in the composition ranges $0 \leq x \leq$ 0.26, and $0.35 \leq x \leq1$ is found to be rhombohedral (R3m) and tetragonal (P4mm), respectively. These results are compared with the predictions of Vanderbilt & Cohen's theory.Comment: 20 pages, 11 pdf figure