3 research outputs found
Osteoinductive Moldable and Curable Bone Substitutes Based on Collagen, BMP-2 and Highly Porous Polylactide Granules, or a Mix of HAP/β-TCP
In dentistry, maxillofacial surgery, traumatology, and orthopedics, there is a need to use osteoplastic materials that have not only osteoinductive and osteoconductive properties but are also convenient for use. In the study, compositions based on collagen hydrogel were developed. Polylactide granules (PLA) or a traditional bone graft, a mixture of hydroxyapatite and β-tricalcium phosphate (HAP/β-TCP), were used for gel filling to improve mechanical osteoconductive properties of compositions. The mechanical tests showed that collagen hydrogels filled with 12 wt% highly porous PLA granules (elastic modulus 373 ± 55 kPa) or 35 wt% HAP/β-TCP granules (elastic modulus 451 ± 32 kPa) had optimal manipulative properties. All composite components were cytocompatible. The cell’s viability was above 90%, and the components’ structure facilitated the cell’s surface adhesion. The bone morphogenetic protein-2 (BMP-2) provided osteoinductive composition properties. It was impregnated directly into the collagen hydrogel with the addition of fibronectin or inside porous PLA granules. The implantation of a collagen hydrogel with BMP-2 and PLA granules into a critical-size calvarial defect in rats led to the formation of the most significant volume of bone tissue: 61 ± 15%. It was almost 2.5 times more than in the groups where a collagen-fibronectin hydrogel with a mixture of HAP/β-TCP (25 ± 7%) or a fibronectin-free composition with porous PLA granules impregnated with BMP-2 (23 ± 8%) were used. Subcutaneous implantation of the compositions also showed their high biocompatibility and osteogenic potential in the absence of a bone environment. Thus, the collagen-fibronectin hydrogel with BMP-2 and PLA granules has optimal biocompatibility, osteogenic, and manipulative properties
Comparative Efficiency of Gene-Activated Matrices Based on Chitosan Hydrogel and PRP Impregnated with <i>BMP2</i> Polyplexes for Bone Regeneration
Gene therapy is one of the most promising approaches in regenerative medicine. Gene-activated matrices provide stable gene expression and the production of osteogenic proteins in situ to stimulate osteogenesis and bone repair. In this study, we developed new gene-activated matrices based on polylactide granules (PLA) impregnated with BMP2 polyplexes and included in chitosan hydrogel or PRP-based fibrin hydrogel. The matrices showed high biocompatibility both in vitro with mesenchymal stem cells and in vivo when implanted intramuscularly in rats. The use of porous PLA granules allowed the inclusion of a high concentration of polyplexes, and the introduction of the granules into hydrogel provided the gradual release of the plasmid constructs. All gene-activated matrices showed transfecting ability and ensured long-term gene expression and the production of target proteins in vitro. At the same time, the achieved concentration of BMP-2 was sufficient to induce osteogenic differentiation of MSCs. When implanted into critical-size calvarial defects in rats, all matrices with BMP2 polyplexes led to new bone formation. The most significant effect on osteoinduction was observed for the PLA/PRP matrices. Thus, the developed gene-activated matrices were shown to be safe and effective osteoplastic materials. PLA granules and PRP-based fibrin hydrogel containing BMP2 polyplexes were shown to be the most promising for future applications in bone regeneration
Osteoinductive Moldable and Curable Bone Substitutes Based on Collagen, BMP-2 and Highly Porous Polylactide Granules, or a Mix of HAP/β-TCP
In dentistry, maxillofacial surgery, traumatology, and orthopedics, there is a need to use osteoplastic materials that have not only osteoinductive and osteoconductive properties but are also convenient for use. In the study, compositions based on collagen hydrogel were developed. Polylactide granules (PLA) or a traditional bone graft, a mixture of hydroxyapatite and β-tricalcium phosphate (HAP/β-TCP), were used for gel filling to improve mechanical osteoconductive properties of compositions. The mechanical tests showed that collagen hydrogels filled with 12 wt% highly porous PLA granules (elastic modulus 373 ± 55 kPa) or 35 wt% HAP/β-TCP granules (elastic modulus 451 ± 32 kPa) had optimal manipulative properties. All composite components were cytocompatible. The cell’s viability was above 90%, and the components’ structure facilitated the cell’s surface adhesion. The bone morphogenetic protein-2 (BMP-2) provided osteoinductive composition properties. It was impregnated directly into the collagen hydrogel with the addition of fibronectin or inside porous PLA granules. The implantation of a collagen hydrogel with BMP-2 and PLA granules into a critical-size calvarial defect in rats led to the formation of the most significant volume of bone tissue: 61 ± 15%. It was almost 2.5 times more than in the groups where a collagen-fibronectin hydrogel with a mixture of HAP/β-TCP (25 ± 7%) or a fibronectin-free composition with porous PLA granules impregnated with BMP-2 (23 ± 8%) were used. Subcutaneous implantation of the compositions also showed their high biocompatibility and osteogenic potential in the absence of a bone environment. Thus, the collagen-fibronectin hydrogel with BMP-2 and PLA granules has optimal biocompatibility, osteogenic, and manipulative properties