Annealing of radiation damage in low resistivity silicon solar cells

The reduction of the temperatures required to restore cell performance after irradiation was investigated with emphasis on the annealing characteristics of two groups of cells containing different amounts of oxygen and carbon. Examination of defect behavior in irradiated boron doped silicon leads to the tentative conclusion that further reduction in annealing temperature could be achieved by decreasing the carbon concentration and either neutralizing the divacancy and/or minimizing its formation as a result of irradiation. A significant reduction in the temperature required to remove radiation induced degradation in 0.1 ohm centimeter silicon solar cells was achieved

Reverse annealing in radiation-damaged, silicon solar cells

In order to understand the results in terms of properties of the radiation induced defects, a combination of diffusion length measurements and defect data obtained from Deep Level Transient Spectroscopy were used. The results indicate that the defect at E sub v + 0.30 eV is responsible for the observed reversed annealing. The defect was identified as a boron-oxygen vacancy complex. This identification is a guide to processing efforts aimed at increasing the concentration of these radiation induced defects

Annealing of radiation damage in 0.1- and 2-ohm-centimeter Silicon solar cells

Isochronal and isothermal annealing studies were conducted on 0.1 and 2 ohm centimeter n(+)/p silicon cells after irradiation by 1 MeV electrons at fluences of 10 to the 14th power, 5 times 10 to the 14th power, and 10 to the 15th power per square centimeter. For the 0.1 ohm centimeter cells, reverse annealing was not observed in the isochronal data. However, reverse annealing was observed between approximately 200 and 325 C in the isochronal data of the 2 ohm centimeter cells. Isothermal annealing of 0.1 ohm centimeter cells at 500 C restored pre-irradiation maximum power P sub max within 20 minutes at fluence = 10 to the 14th power, in 180 minutes at fluence = 5 times 10 to the 14th power and to 92 percent of pre-irradiation P sub max in 180 minutes for fluence = 10 to the 15th power. Annealing at 450 C was found inadequate to restore 0.1 ohm centimeter cell performance within reasonable times for all fluence levels. By comparison, at 450 C, the P sub max of 2 ohm centimeter cells was restored within 45 minutes, for the two highest fluence levels, while for the lowest fluence, restoration was completed within 15 minutes. Spectral response data indicate that, for both resistivities, degradation occurs predominantly in the cells p-type base region

Radiation damage annealing mechanisms and possible low temperature annealing in silicon solar cells

The defect responsible for reverse annealing in 2 ohm/cm n(+)/p silicon solar cells was identified. This defect, with energy level at e sub v + 0.30 eV was tentatively identified as a boron oxygen-vacancy complex. Results indicate that its removal could result in significant annealing for 2 ohm/cm and lower resistivity cells at temperatures as low as 200 C. These results were obtained by use of an expression derived from the Shockley-Read-Hall recombination theory which relates measured diffusion length ratios to relative defect concentrations and electron capture cross sections. The relative defect concentrations and one of the required capture cross sections are obtained from Deep Level Transient Spectroscopy. Four additional capture cross sections are obtained using diffusion length data and data from temperature dependent lifetime studied. These calculated results are in reasonable agreement with experimental data

Radiation damage in high-resistivity silicon solar cells

High-resistivity silicon solar cells exhibit reduced radiation damage when light is incident on the gridded back surface. Under back illumination, radiation damage decreases as cell resistivity increases; under front illumination, radiation damage increases as cell resistivity increases. Thin back-illuminated cells outperform conventional 10 omega cm 50 and 200 micron cells at low 1-MeV electron fluences. However, at higher fluences, the conventional cells exhibit superior radiation resistance. This is attributed to the low BOL diffusion lengths observed in the thin, sack-illuminated cell. These results are discussed in terms of injected charge distributions, electric fields in the cell base, and the effects of a dominant boron-oxygen defect

Reduced annealing temperatures in silicon solar cells

Cells irradiated to a fluence of 5x10,000,000,000,000/square cm showed short circuit current on annealing at 200 C, with complete annealing occurring at 275 C. Cells irradiated to 100,000,000,000,000/square cm showed a reduction in annealing temperature from the usual 500 to 300 C. Annealing kinetic studies yield an activation energy of (1.5 + or - 2) eV for the low fluence, low temperature anneal. Comparison with activation energies previously obtained indicate that the presently obtained activation energy is consistent with the presence of either the divacancy or the carbon interstitial carbon substitutional pair, a result which agrees with the conclusion based on defect behavior in boron-doped silicon

Performance of Hughes GaAs concentrator cells under 1-MeV electron irradiation

Several Hughes gallium arsenide (GaAs) concentrator cells were exposed to 1-MeV electrons at fluences up to 1x10 to the 15th power electrons/sq cm. Performance data were taken after several fluences, at two temperatures, and at concentration levels from 1 to approx. 150x AMO. Data at 1 sun and 25 deg C were taken with an X-25 xenon-lamp solar simulator. Data at concentration were taken using a pulsed solar simulator with the assumption of a linear relationship between short-circuit current and irradiance. The cells are 5 by 5 mm with a 4-mm diameter illuminated area

Preliminary evaluation of Glass Resin materials for solar cell cover use

The glass resins were deposited by several techniques on 200 micron thick cells and on 50 microns thick wafers. The covered cells were exposed to ultraviolet light in vacuum to an intensity of 10 UV energy-equivalent solar constants at air mass zero for 728 hr. The exposure was followed by a single long thermal cycle from ambient temperature to -150 C. Visual inspection of the samples indicated that all samples had darkened to varying degrees. The loss in short-circuit current was found to range from 8 to 24%, depending on the resin formulation. In another test over 40 glass resin-coated silicon wafers withstood 15 thermal cycles from 100 to-196 C in one or more of the thicknesses tested. Several of the resin-coated wafers were tested at 65 C and 90% relative humidity for 170 hr. No change in physical appearance was detected

Radiation damage and defect behavior in ion-implanted, lithium counterdoped silicon solar cells

Boron doped silicon n+p solar cells were counterdoped with lithium by ion implanation and the resultant n+p cells irradiated by 1 MeV electrons. The function of fluence and a Deep Level Transient Spectroscopy (DLTS) was studied to correlate defect behavior with cell performance. It was found that the lithium counterdoped cells exhibited significantly increased radiation resistance when compared to boron doped control cells. It is concluded that the annealing behavior is controlled by dissociation and recombination of defects. The DLTS studies show that counterdoping with lithium eliminates at least three deep level defects and results in three new defects. It is speculated that the increased radiation resistance of the counterdoped cells is due primarily to the interaction of lithium with oxygen, single vacancies and divacancies and that the lithium-oxygen interaction is the most effective in contributing to the increased radiation resistance

Temperature and intensity dependence of the performance of an electron-irradiated (AlGa)As/GaAs solar cell

The performance of a Hughes, liquid-phase epitaxial 2 centimeter-by-2 centimeter, (AlGa)As/GaAs solar cell was measured before and after irradiations with 1 MeV electrons to fluences of 1 x 10 to the 16th power electrons/sq cm. The temperature dependence of performance was measured over the temperature range 135 to 415 K at each fluence level. In addition, temperature dependences were measured at five intensity levels from 137 to 2.57 mW/sq cm before irradiation and after a fluence of 1 x 10 to the 16th power electrons/sq cm. For the intermediate fluences, performance was measured as a function of intensity at 298 K only