Spannungsrisskorrosion an austenitischem Gusseisen in MgCl_2-Loesung
Since austenitic cast iron is not a passive material, cracks in construction of cast iron most were assumed to be defects of fabrication. First investigation showed, that this material is susceptible to stress corrosion cracking. With round-bar specimens of GGG NiCr 20 2 and GGG NiCr 30 3 in MgCl_2-solution with variable concentration, temperature and applied stress diagramms of susceptibility were established. GGG NiCr 30 3 is more resistance than GGG NiCr 20 2. For both kind of cast iron exist a limit of tensile stress below no more stress corrosion cracking occurred. The most effective method for protection of austenitic cast iron is a reduction in stress by stress relief heat treatment. (orig.)Da austenitische Gusseisensorten als nicht passive Werkstoffe gelten, wurden Rissschaeden meist auf Herstellungsfehler zurueckgefuehrt. Vorversuche zeigten jedoch, dass diese Werkstoffe in chloridhaltigen Medien Spannungsrisskorrosion erleiden koennen. An Zugstaeben von GGG NiCr 20 2 und GGG NiCr 30 3 wurden in MgCl_2-Loesung unterschiedlicher Konzentration, Temperatur und Zugspannung Bestaendigkeits- bzw. Anfaelligkeitsschaubilder aufgenommen. GGG NiCr 30 3 ist bestaendiger gegenueber Spannungsrisskorrosion als GGG NiCr 20 2. Es gibt fuer beide Gusssorten Grenzwerte der Zugspannung, unterhalb denen keine Spannungsrisskorrosion mehr auftritt. Spannungsarmgluehen ist daher das beste Mittel um Spannungsrisskorrosion zu vermeiden. (orig.)Available from TIB Hannover: FR 5389 / FIZ - Fachinformationszzentrum Karlsruhe / TIB - Technische InformationsbibliothekSIGLEBundesministerium fuer Forschung und Technologie (BMFT), Bonn (Germany)DEGerman
Lebensdauerberechnung fuer inhomogen beanspruchte Bauteile mit Randschicht und Eigenspannung
TIB Hannover: RO 1533(1989,16) / FIZ - Fachinformationszzentrum Karlsruhe / TIB - Technische InformationsbibliothekSIGLEDEGerman