Люминесценция и рассеяние света в допированных стеклах ZBLAN и теллуритных стеклах
Some ZBLAN glasses doped with NdF3 and the tellurium-containing glass 90TeO2–10PbO∙P2O5 were
studied by physical chemical methods. The temperature dependence of luminescence intensity was
obtained for the ZBLAN glasses. Light scattering of ZBLAN glasses and the tellurium-containing
glass was studied. The luminescence maximum (1054 nm, Nd) and the scattered light maximum (1100
nm) were recorded in the temperature range 25–440°C for the ZBLAN glasses and 25–530°C for the
tellurium-containing glass. The correlation was found between temperature changes in the optical
characteristics and data of differential thermal analysis of the glasses. It was shown that in the optical
temperature dependences there were observed changes in the area of glass transition temperature
Tg, the onset of crystallization Tx and maximum crystallization Tc. It is possible to use the temperature
dependences of optical curves as a control for heat treatment of vitreous samples at glass ceramics
productionФизико-химическими методами изучены некоторые стекла ZBLAN, допированные NdF3, и
теллурсодержащее стекло 90TeO2–10PbO∙P2O5. Для стекол ZBLAN получена температурная
зависимость интенсивности люминесценции. Исследовано рассеяние света в стеклах
ZBLAN и в теллурсодержащем стекле. Максимумы люминесценции (1054 нм, Nd) и рассеяния
света (1100 nm) определены в диапазонах температур 25–440 °C для стекол ZBLAN и
25–530°C для теллурсодержащего стекла. Обнаружена корреляция между температурными
изменениями оптических характеристик и данными дифференциального термического
анализа рассмотренных стекол. Показано, что в температурных зависимостях оптических
характеристик наблюдаются изменения в области температур стеклования Tg, начала
кристаллизации Tx и максимума кристаллизации Tc. Возможно использование температурных
зависимостей оптических кривых для контроля термообработки стеклянных образцов при
получении стеклокерамик
Люминесценция и рассеяние света в допированных стеклах ZBLAN и теллуритных стеклах
Some ZBLAN glasses doped with NdF3 and the tellurium-containing glass 90TeO2–10PbO∙P2O5 were
studied by physical chemical methods. The temperature dependence of luminescence intensity was
obtained for the ZBLAN glasses. Light scattering of ZBLAN glasses and the tellurium-containing
glass was studied. The luminescence maximum (1054 nm, Nd) and the scattered light maximum (1100
nm) were recorded in the temperature range 25–440°C for the ZBLAN glasses and 25–530°C for the
tellurium-containing glass. The correlation was found between temperature changes in the optical
characteristics and data of differential thermal analysis of the glasses. It was shown that in the optical
temperature dependences there were observed changes in the area of glass transition temperature
Tg, the onset of crystallization Tx and maximum crystallization Tc. It is possible to use the temperature
dependences of optical curves as a control for heat treatment of vitreous samples at glass ceramics
productionФизико-химическими методами изучены некоторые стекла ZBLAN, допированные NdF3, и
теллурсодержащее стекло 90TeO2–10PbO∙P2O5. Для стекол ZBLAN получена температурная
зависимость интенсивности люминесценции. Исследовано рассеяние света в стеклах
ZBLAN и в теллурсодержащем стекле. Максимумы люминесценции (1054 нм, Nd) и рассеяния
света (1100 nm) определены в диапазонах температур 25–440 °C для стекол ZBLAN и
25–530°C для теллурсодержащего стекла. Обнаружена корреляция между температурными
изменениями оптических характеристик и данными дифференциального термического
анализа рассмотренных стекол. Показано, что в температурных зависимостях оптических
характеристик наблюдаются изменения в области температур стеклования Tg, начала
кристаллизации Tx и максимума кристаллизации Tc. Возможно использование температурных
зависимостей оптических кривых для контроля термообработки стеклянных образцов при
получении стеклокерамик