Strain specificity in antimicrobial activity of silver and copper nanoparticles

The antimicrobial properties of silver and copper nanoparticles were investigated using Escherichia coli (four strains), Bacillus subtilis and Staphylococcus aureus (three strains). The average sizes of the silver and copper nanoparticles were 3 nm and 9 nm, respectively, as determined through transmission electron microscopy. Energy-dispersive X-ray spectra of silver and copper nanoparticles revealed that while silver was in its pure form, an oxide layer existed on the copper nanoparticles. The bactericidal effect of silver and copper nanoparticles were compared based on diameter of inhibition zone in disk diffusion tests and minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) of nanoparticles dispersed in batch cultures. Bacterial sensitivity to nanoparticles was found to vary depending on the microbial species. Disk diffusion studies with E. coli and S. aureus revealed greater effectiveness of the silver nanoparticles compared to the copper nanoparticles. B. subtilis depicted the highest sensitivity to nanoparticles compared to the other strains and was more adversely affected by the copper nanoparticles. Good correlation was observed between MIC and MBC (r2 = 0.98) measured in liquid cultures. For copper nanoparticles a good negative correlation was observed between the inhibition zone observed in disk diffusion test and MIC/MBC determined based on liquid cultures with the various strains (r2 = −0.75). Although strain-specific variation in MIC/MBC was negligible for S. aureus, some strain-specific variation was observed for E. coli.© Elsevie

Potential of carbon nanomaterials for removal of heavy metals from water

Heavy metals, such as, cadmium, lead, nickel and zinc can be removed from water using sorbents. The rate and extent of removal may be enhanced by choice of appropriate sorbents. In this study heavy metal sorption was studied on indigenously synthesized carbon nanomaterials (CNMs). Two CNMs differing in surface morphology were synthesized using turpentine oil in a chemical vapour deposition (CVD) setup by varying the process parameters. Activation and catalyst removal were achieved by post-treatment with HNO3 and KOH. Characterization of the CNMs produced revealed that both comprised of graphitic amorphous carbon, however, while the nanocarbon (NC) produced using cobalt catalyst in N2 atmosphere comprised of varying grain sizes indicative of soot, the nanoporous carbon (NPC) produced using silica catalyst in H2 atmosphere had a distinctive uniformly porous surface morphology. Comparative sorption studies with cadmium, lead, nickel and zinc also revealed greater sorption on NPC compared to NC. Batch isotherms for the various heavy metals using NPC and a commercial activated carbon (AC) widely used for metal sorption revealed that NPC is characterized by significantly higher metal sorption capacity and more favourable sorption energetics. The superior performance of NPC as a sorbent may be due to its unique nanoporous structure.© Elsevie