250 research outputs found

    Characterising Solder Materials from Random Vibration Response of their Interconnects in BGA Packaging

    Get PDF
    Solder interconnection in electronic packaging is the weakest link, thus driving the reliability of electronic modules and systems. Improving interconnection integrity in safety-critical applications is vital in enhancing application reliability. This investigation qualifies the random vibration response of five essential solder compositions in ball grid array (BGA) solder joints used in safety-critical applications. The solder compositions are eutectic Sn63Pb37 and SnAgCu (SAC) 305, 387, 396, and 405. Computer-aided engineering (CAE) employing ANSYS FEA and SolidWorks software is implemented in this investigation. The solder Sn63Pb37 deformed least at 0.43 µm, followed by SAC396 at 0.58 µm, while SAC405 deformed highest at 0.88 µm. Further analysis demonstrates that possession of higher elastic modulus and mass density culminates in lower solder joint deformation. Stress is concentrated at the periphery of the solder joints in contact with the printed circuit board (PCB). The SAC396 solder accumulates the lowest stress of 14.1 MPa, followed by SAC405 at 17.9 MPa, while eutectic Sn63Pb37 accrues the highest at 34.6 MPa. Similarly, strain concentration is found at the interface between the solder joint and copper pad on PCB. SAC405 acquires the lowest elastic strain magnitude of 0.0011 mm/mm, while SAC305 records the highest strain of 0.002 mm/mm. These results demonstrate that SAC405 solder has maximum and SAC387 solder has minimum fatigue lives

    Effective Solder for Improved Thermo-Mechanical Reliability of Solder Joints in a Ball Grid Array (BGA) Soldered on Printed Circuit Board (PCB)

    Get PDF
    Ball grid array (BGA) packages have increasing applications in mobile phones, disk drives, LC displays and automotive engine controllers. However, the thermo-mechanical reliability of the BGA solder joints challenges the device functionality amidst component and system miniaturisation as well as wider adoption of lead-free solders. This investigation determines the effective BGA solders for improved thermo-mechanical reliability of the devices. It utilised a conducted study on creep response of a lead-based eutectic Sn63Pb37 and four lead-free Tin-Silver-Copper (SnAgCu) [SAC305, SAC387, SAC396 and SAC405] solders subjected to thermal cycling loadings and isothermal ageing. The solders form the joints between the BGAs and printed circuit boards (PCBs). ANSYS R19.0 package is used to simulate isothermal ageing of some of the assemblies at -40℃, 25℃, 75℃ and 150℃ temperatures for 45 days and model the thermal cycling history of the other assemblies from 22℃ ambient temperature for six cycles. The response of the solders is simulated using Garofalo-Arrhenius creep model. Under thermal ageing, SAC396 solder joints demonstrate possession of least strain energy density, deformation and von-Mises stress in comparison to the other solders. Under thermal cycle loading conditions, SAC405 acquired the lowest amount of the damage parameters in comparison. Lead-free SAC405 and SAC387 joints accumulated the lowest and highest energy dissipation per cycle, respectively. It is concluded that SAC405 and SAC396 are the most effective solders for BGA in devices experiencing isothermal ageing and temperature cycling during operation, respectively. They are proposed as the suitable replacement of eutectic Sn63Pb37 solder for the various conditions.University of Derb

    A Finite Element approach to understanding constitutive elasto-plastic, visco-plastic behaviour in lead free micro-electronic BGA structures

    Get PDF
    This work investigates the non-linear elasto-plastic and visco-plastic behaviour of lead free solder material and soldered joints. Specifically, Finite Element (FE) tools were used to better understand the deformations within Ball Grid Array solder joints (BGA), and numerical and analytical methods were developed to quantify the identified constituent deformations. FE material models were based on the same empirical constitutive models (elastic, plastic and creep) used in analytical calculations. The current work recognises the large number of factors influencing material behaviour which has led to a wide range of published material properties for near eutectic SnAgCu alloys. The work discovered that the deformation within the BGA was more complex than is generally assumed in the literature. It was shown that shear deformation of the solder ball could account for less than 5% of total measured displacement in BGA samples. Shear displacement and rotation of the solder balls relative to the substrate are sensitive to the substrate orthotropic properties and substrate geometry (relative to solder volume and array pattern). The FE modelling was used to derive orthotropic FR4 properties independently using published data. An elastic modulus for Sn3.8Ag0.7Cu was measured using homologous temperatures below 0.3. Suggested values of Abaqus-specific creep parameters m and f (not found in literature) for Sn3.8Ag0.7Cu have been validated with published data. Basic verification against simple analytical calculations has given a better understanding of the components of overall specimen displacement that is normally missing from empirical validation alone. A combined approach of numerical and analytical modelling of BGAs, and mechanical tests, is recommended to harmonise published work, exploit new material data and for more informed analysis of new configurationsEPSRC-funded PhD studentshi

    Numerical analysis of lead-free solder joints: effects of thermal cycling and electromigration

    Get PDF
    To meet the requirements of miniaturization and multifunction in microelectronics, understanding of their reliability and performance has become an important research subject in order to characterise electronics served under various loadings. Along with the demands of the increasing miniaturization of electronic devices, various properties and the relevant thermo-mechanical-electrical response of the lead-free solder joints to thermal cycling and electro-migration become the critical factors, which affect the service life of microelectronics in different applications. However, due to the size and structure of solder interconnects in microelectronics, traditional methods based on experiments are not applicable in the evaluation of their reliability under complex joint loadings. This thesis presents an investigation, which is based on finite-element method, into the performance of lead-free solder interconnects under thermal fatigue and electro-migration, specifically in the areas as follows: (1) the investigation of thermal-mechanical performance and fatigue-life prediction of flip-chip package under different sizes to achieve a further understanding of IMC layer and size effects of a flip chip package under thermal cycling; (2) the establishment of a numerical method, simulating void-formation/crack-propagation based on the results of finite-element analysis, to allow the prediction of crack evolution and failure time for electro-migration reliability of solder bumps; (3) the establishment of a flow-based algorithm for combination effects of thermal-mechanical and electro-migration that was subsequent implemented in to an FE model to evaluate the reliability assessment of service lives associated with a flip chip package

    The durability of solder joints under thermo-mechanical loading; application to Sn-37Pb and Sn-3.8Ag-0.7Cu lead-free replacement alloy

    Get PDF
    Solder joints in electronic packages provide mechanical, electrical and thermal connections. Hence, their reliability is also a major concern to the electronic packaging industry. Ball Grid Arrays (BGAs) are a very common type of surface mount technology for electronic packaging. This work primarily addresses the thermo-mechanical durability of BGAs and is applied to the exemplar alloys; traditional leaded solder and a popular lead-free solder. Isothermal mechanical fatigue tests were carried out on 4-ball test specimens of the lead-free (Sn-3.8Ag-0.7Cu) and leaded (Sn-37Pb) solder under load control at room temperature, 35°C and 75°C. As well as this, a set of combined thermal and mechanical cycling tests were carried out, again under load control with the thermal cycles either at a different frequency from the mechanical cycles (not-in-phase) or at the same frequency (both in phase and out-of-phase). The microstructural evaluation of both alloys was investigated by carrying out a series of simulated ageing tests, coupled with detailed metallurgical analysis and hardness testing. The results were treated to produce stress-life, cyclic behaviour and creep curves for each of the test conditions. Careful calibration allowed the effects of substrate and grips to be accounted for and so a set of strain-life curves to be produced. These results were compared with other results from the literature taking into account the observations on microstructure made in the ageing tests. It is generally concluded that the TMF performance is better for the Sn-Ag-Cu alloy than for the Sn-Pb alloy, when expressed as stress-life curves. There is also a significant effect on temperature and phase for each of the alloys, the Sn-Ag-Cu being less susceptible to these effects. When expressed as strain life, the effects of temperature, phase and alloy type are much diminished. Many of these conclusions coincided with only parts of the literature and reasons for the remaining differences are advanced

    COMPARISON OF INTERCONNECT FAILURES OF ELECTRONIC COMPONENTS MOUNTED ON FR-4 BOARDS WITH SN37PB AND SN3.0AG0.5CU SOLDERS UNDER RAPID LOADING CONDITIONS.

    Get PDF
    Electronic circuit boards can experience rapid loading through shock or vibration events during their lives; these events can happen in transportation, manufacture, or in field conditions. Due to the lead-free migration, it is necessary to evaluate how this rapid loading affects the durability of a leading lead free solder alternative (Sn3.0Ag0.5Cu) assemblies as compared with traditional eutectic lead based solder Sn37Pb assemblies. A literature review showed that there is little agreement on the fatigue behavior of Sn37Pb solder assemblies and Sn3.0Ag0.5Cu solder assemblies subjected to rapid loading. To evaluate the failure behavior of Sn37Pb and Sn3.0Ag0.5Cu solder assemblies under rapid loading conditions, leadless chip resistors (LCR), ball grid arrays (BGA), small outline integrated circuits (SOIC), and small outline transistors (SOT) were subjected to four point bend tests via a servo-hydraulic testing machine at printed wiring board (PWB) strain rates greater than 0.1/s. The PWB strain was the metric used to evaluate the failures. The PBGAs and LCRs were examined with both Sn37Pb and Sn3.0Ag0.5Cu solders. There was no significant difference found in the resulting test data for the behavior of the two solder assembly types in the high cycle fatigue regime. PBGA assemblies with both solders were also evaluated at a higher strain rate, approximately 1/s, using drop testing. There was no discernable difference found between the assemblies as well as no difference in the failure rate of the PBGAs at this higher strain rate. The PWB strain was converted to an equivalent solder stress index using finite element analysis. This equivalent stress index value was used to compare the results from the LCR and BGA testing for Sn37Pb and Sn3.0Ag0.5Cu. Independently generated BGA data that differed with respect to many testing variables was adjusted and incorporated to this comparison. The resulting plot did not show any significant differences between the behaviors of the two solder assemblies under rapid loading outside of the ultra low cycle fatigue regime, where the assemblies with Sn37Pb solder outperformed the assemblies with SnAgCu solder

    Thermo-mechanical reliability studies of lead-free solder interconnects

    Get PDF
    N/ASolder interconnections, also known as solder joints, are the weakest link in electronics packaging. Reliability of these miniature joints is of utmost interest - especially in safety-critical applications in the automotive, medical, aerospace, power grid and oil and drilling sectors. Studies have shown that these joints' critical thermal and mechanical loading culminate in accelerated creep, fatigue, and a combination of these joints' induced failures. The ball grid array (BGA) components being an integral part of many electronic modules functioning in mission-critical systems. This study investigates the response of solder joints in BGA to crucial reliability influencing parameters derived from creep, visco-plastic and fatigue damage of the joints. These are the plastic strain, shear strain, plastic shear strain, creep energy density, strain energy density, deformation, equivalent (Von-Mises) stress etc. The parameters' obtained magnitudes are inputted into established life prediction models – Coffin-Manson, Engelmaier, Solomon (Low cycle fatigue) and Syed (Accumulated creep energy density) – to determine several BGA assemblies' fatigue lives. The joints are subjected to thermal, mechanical and random vibration loadings. The finite element analysis (FEA) is employed in a commercial software package to model and simulate the responses of the solder joints of the representative assemblies' finite element models. As the magnitude and rate of degradation of solder joints in the BGA significantly depend on the composition of the solder alloys used to assembly the BGA on the printed circuit board, this research studies the response of various mainstream lead-free Sn-Ag-Cu (SAC) solders (SAC305, SAC387, SAC396 and SAC405) and benchmarked those with lead-based eutectic solder (Sn63Pb37). In the creep response study, the effects of thermal ageing and temperature cycling on these solder alloys' behaviours are explored. The results show superior creep properties for SAC405 and SAC396 lead-free solder alloys. The lead-free SAC405 solder joint is the most effective solder under thermal cycling condition, and the SAC396 solder joint is the most effective solder under isothermal ageing operation. The finding shows that SAC405 and SAC396 solders accumulated the minimum magnitudes of stress, strain rate, deformation rate and strain energy density than any other solder considered in this study. The hysteresis loops show that lead-free SAC405 has the lowest dissipated energy per cycle. Thus the highest fatigue life, followed by eutectic lead-based Sn63Pb37 solder. The solder with the highest dissipated energy per cycle was lead-free SAC305, SAC387 and SAC396 solder alloys. In the thermal fatigue life prediction research, four different lead-free (SAC305, SAC387, SAC396 and SAC405) and one eutectic lead-based (Sn63Pb37) solder alloys are defined against their thermal fatigue lives (TFLs) to predict their mean-time-to-failure for preventive maintenance advice. Five finite elements (FE) models of the assemblies of the BGAs with the different solder alloy compositions and properties are created with SolidWorks. The models are subjected to standard IEC 60749-25 temperature cycling in ANSYS 19.0 mechanical package environment. SAC405 joints have the highest predicted TFL of circa 13.2 years, while SAC387 joints have the least life of circa 1.4 years. The predicted lives are inversely proportional to the magnitude of the areas of stress-strain hysteresis loops of the solder joints. The prediction models are significantly consistent in predicted magnitudes across the solder joints irrespective of the damage parameters used. Several failure modes drive solder joints and damage mechanics from the research and understand an essential variation in the models' predicted values. This investigation presents a method of managing preventive maintenance time of BGA electronic components in mission-critical systems. It recommends developing a novel life prediction model based on a combination of the damage parameters for enhanced prediction. The FEA random vibration simulation test results showed that different solder alloys have a comparable performance during random vibration testing. The fatigue life result shows that SAC405 and SAC396 have the highest fatigue lives before being prone to failure. As a result of the FEA simulation outcomes with the application of Coffin-Manson's empirical formula, the author can predict the fatigue life of solder joint alloys to a higher degree of accuracy of average ~93% in an actual service environment such as the one experienced under-the-hood of an automobile and aerospace. Therefore, it is concluded that the combination of FEA simulation and empirical formulas employed in this study could be used in the computation and prediction of the fatigue life of solder joint alloys when subjected to random vibration. Based on the thermal and mechanical responses of lead-free SAC405 and SAC396 solder alloys, they are recommended as a suitable replacement of lead-based eutectic Sn63Pb37 solder alloy for improved device thermo-mechanical operations when subjected to random vibration (non-deterministic vibration). The FEA simulation studies' outcomes are validated using experimental and analytical-based reviews in published and peer-reviewed literature.N/

    Development of a Rapid Fatigue Life Testing Method for Reliability Assessment of Flip-Chip Solder Interconnects

    Get PDF
    The underlying physics of failure are critical in assessing the long term reliability of power packages in their intended field applications, yet traditional reliability determination methods are largely inadequate when considering thermomechanical failures. With current reliability determination methods, long test durations, high costs, and a conglomerate of concurrent reliability degrading threat factors make effective understanding of device reliability difficult and expensive. In this work, an alternative reliability testing apparatus and associated protocol was developed to address these concerns; targeting rapid testing times with minimal cost while preserving fatigue life prediction accuracy. Two test stands were fabricated to evaluate device reliability at high frequency (60 cycles/minute) with the first being a single-directional unit capable of exerting large forces (up to 20 N) on solder interconnects in one direction. The second test stand was developed to allow for bi-directional application of stress and the integration of an oven to enable testing at elevated steady-state temperatures. Given the high frequency of testing, elevated temperatures are used to emulate the effects of creep on solder fatigue lifetime. Utilizing the mechanical force of springs to apply shear loads to solder interconnects within the devices, the reliability of a given device to withstand repeated cycling was studied using resistance monitoring techniques to detect the number of cycles-to-failure (CTF). Resistance monitoring was performed using specially designed and fabricated, device analogous test vehicles assembled with the ability to monitor circuit resistance in situ. When a resistance rise of 30 % was recorded, the device was said to have failed. A mathematical method for quantifying the plastic work density (amount of damage) sustained by the solder interconnects prior to failure was developed relying on the relationship between Hooke’s Law for springs and damage deflection to accurately assess the mechanical strength of tested devices

    MODELING RATE DEPENDENT DURABILITY OF LOW-Ag SAC INTERCONNECTS FOR AREA ARRAY PACKAGES UNDER TORSION LOADS

    Get PDF
    The thesis discusses modeling rate-dependent durability of solder interconnects under mechanical torsion loading for surface mount area array components. The study discusses an approach to incorporate strain-rate dependency in durability estimation for solder interconnects. The components under study are two configurations of BGAs (ball grid array) assembled with select lead-free solders. A torsion test setup is used to apply displacement controlled loads on the test board. Accelerated test load profile is experimentally determined. Torsion test is carried out for all the components under investigation to failure. Strain-rate dependent (Johnson-Cook model) and strain-rate independent, elastic-plastic properties are used to model the solders in finite element simulation. Damage model from literature is used to estimate the durability for SAC305 solder to validate the approach. Test data is used to extract damage model constants for SAC105 solder and extract mechanical fatigue durability curve
    • …