Failure Analysis and Recovery of a 50mm Highly Elastic Intermetallic NiTi Ball Bearing for an ISS Application

Abstract

The ISS Distillation Assembly centrifuge is the pathfinder application for 50mm bore, deep-groove ball bearings made from the highly elastic intermetallic material 60NiTi. Superior corrosion and shock resistance are required to withstand the acidic wastewater exposure and heavy spacecraft launch related loads that challenge conventional steel bearings. During early ground testing one bearing unexpectedly and catastrophically failed after operating for only 200 hours of run time. A second bearing running on the same shaft was completely unaffected. A thorough investigation into the root cause of the failure determined that an excessively tight press-fit of the bearing outer race coupled with NiTis relatively low elastic modulus were key contributing factors. The proposed failure mode was successfully duplicated by experiment. To further corroborate the root cause theory, a successful bearing life test using improved installation practices (selective fitting) was conducted. The results show that NiTi bearings are suitable for space applications provided that care is taken to accommodate their unique material characteristics