High-performance 4H-SiC-based ultraviolet p-i-n photodetector

Abstract

A high-performance 4H-SiC p-i-n photodetector for visible-blind ultraviolet (UV) applications has been designed and fabricated. The electrical and optical characteristics were measured at room temperature. The photodetector suffered from significant dark current of 2.5 pA/mm(2) at reverse bias of 5 V, and the UV light photocurrent was larger than four orders of magnitude higher than the dark current. The built-in potential and the unintentional i-layer doping concentration were obtained from capacitance-voltage (C-V) measurements. The spectral peak responsivity of the detector reached 0.13 A/W at a wavelength of 270 nm, corresponding to a maximum external quantum efficiency of similar to 61%. And the ratio of responsivity at 270 nm to that at 380 nm was > 10(3). The characteristics imply that the photodetector has a great improved ultraviolet-visible rejection ratio which is needed for ultraviolet signal detection

Similar works

Full text

thumbnail-image

Xiamen University Institutional Repository

Provided original full text link
oaioai:dspace.xmu.edu.cn:2288/91568Last time updated on 6/16/2016

This paper was published in Xiamen University Institutional Repository.

Having an issue?

Is data on this page outdated, violates copyrights or anything else? Report the problem now and we will take corresponding actions after reviewing your request.